Alloys-ka xusuusta qaabaysan (SMAs) waxay leeyihiin jawaab-celin sifada leh oo ku aaddan kicinta heerkulbeegga. Kiciyeyaasha Thermomechanical waxay ka yimaadaan heerkul sare, barokac, isbeddel adag oo adag, iwm. Marxaladda wareegga wareegga ah ee soo noqnoqda waxay keenaysaa koror tartiib tartiib ah ee kala-baxa, sidaas awgeed meelaha aan isbeddelin waxay yareyn doonaan shaqeynta SMA (oo loo yaqaan daalka shaqada) waxayna soo saaraan microcracks, taas oo ugu dambeyntii u horseedi doonta fashilka jireed marka tiradu ay ku filan tahay. Sida iska cad, fahamka dabeecadda nolosha daalka ee Alloys-kan, xallinta dhibaatada qashinka qayb ka mid ah qaaliga ah, iyo yaraynta horumarinta alaabta iyo wareegga naqshadaynta alaabta ayaa dhammaantood dhalin doona cadaadis dhaqaale oo weyn.
Daalka kuleyliyaha-farsamoyaqaanka lama sahamin ilaa xad, gaar ahaan la'aanta cilmi-baaris ku saabsan faafinta dildilaaca daal ee wareegyada kulaylka-farsamoda. Hirgelinta hore ee SMA ee biomedicine, diiradda cilmi-baarista daalku waxay ahayd wadarta nolosha shaybaarada "cilad-la'aanta" ee ka hooseeya culeysyada farsamada wareegga ah. Codsiyada leh joomatari yar oo SMA ah, korriinka dillaaca daalka ayaa saameyn yar ku leh nolosha, sidaas darteed cilmi-baaristu waxay diiradda saartaa ka hortagga bilawga dillaaca halkii ay ka xakamayn lahayd koritaankeeda; wadista, dhimista gariirka iyo codsiyada nuugista tamarta, waa lagama maarmaan in si dhakhso ah loo helo koronto. Qaybaha SMA ayaa inta badan waa weyn oo ku filan si loo ilaaliyo faafinta dillaaca ka hor fashilka. Sidaa darteed, si loo daboolo kalsoonida lagama maarmaanka ah iyo shuruudaha badbaadada, waxaa lagama maarmaan ah in si buuxda loo fahmo oo loo qiyaaso dabeecadda koritaanka daalka ee dillaaca iyada oo loo marayo habka dulqaadka dhaawaca. Codsiga hababka dulqaadka dhaawaca ee ku tiirsan fikradda makaanikada jaban ee SMA ma fududa. Marka la barbar dhigo biraha qaab-dhismeed ee soo jireenka ah, jiritaanka marxaladda kala-guurka ah ee la beddeli karo iyo isku-xidhka-farsamada heerkulbeegga ayaa keenaya caqabado cusub si loo qeexo daalka iyo jabka xad-dhaafka ah ee SMA.
Cilmi-baarayaal ka socda Jaamacadda Texas A&M ee dalka Mareykanka ayaa sameeyay tijaabooyin kororsi koronto ah oo farsameysan iyo daal kexeeyay Ni50.3Ti29.7Hf20 superalloy markii ugu horreysay, waxayna soo jeediyeen qaanuunka awoodda nooca Paris ku saleysan oo loo isticmaali karo Fit the daalka. heerka koritaanka dildilaaca halbeeg ka hooseeya. Waxaa laga soo qaatay tan in xiriirka la taaban karo ee heerka kobaca dillaaca lagu rakibi karo inta u dhexeysa xaaladaha kala duwan ee loading iyo qaabeynta joomatari, taas oo loo isticmaali karo sharraxaadda midaysan ee suurtogalka ah ee koritaanka dildilaaca ee SMA-yada. Warqadda la xidhiidha ayaa lagu daabacay Acta Materialia oo cinwaankeedu yahay "Sharaxaad midaysan oo ku saabsan koritaanka daalka farsamada iyo firfircoonida ee koritaanka qaabka xusuusta".
Xiriirinta warqad:
https://doi.org/10.1016/j.actamat.2021.117155
Daraasadu waxay ogaatay in marka Ni50.3Ti29.7Hf20 daawaha lagu sakhiray tijaabo tensile uniaxial at 180 ℃, austenite inta badan waa laastically qallafsan hoos heerka stress hoose inta lagu guda jiro habka loading, iyo modules Young ayaa ku saabsan 90GPa. Marka diiqadu gaadho qiyaastii 300MPa Bilowga isbeddelka wajiga togan, austenite wuxuu isu beddelaa martensite-ka-soo-baxa; marka la soo dejiyo, martensite-ka kadeedka uu keeno inta badan waxa uu maraa qallafsanaan laastikada ah, oo leh module-ka dhallinta ee ku dhawaad 60 GPa, ka dibna waxa uu dib ugu noqdaa austenite. Iyadoo la adeegsanayo isdhexgalka, heerka korriinka daalka dillaaca ee qalabka dhismaha ayaa lagu rakibay muujinta sharciga awoodda nooca Paris.
Fig.1 sawirka BSE ee Ni50.3Ti29.7Hf20 heerkulka sare ee qaabka xusuusta alloy iyo qaybinta cabbirka qaybaha oksaydhka
Jaantus 2 Sawirka TEM ee Ni50.3Ti29.7Hf20 heerkulka sare ee qaabka xusuusta alloy ka dib daaweynta kulaylka ee 550 ℃ × 3h
Jaantuska 3 Xidhiidhka u dhexeeya J iyo da/dN ee daalka farsamada ee dillaaca korriinka NiTiHf DCT ee 180℃
Tijaabooyin ku jira maqaalkan, waxaa la caddeeyey in qaaciddadani ay ku habboonaan karto xogta heerka koritaanka daal ee dillaaca dhammaan tijaabooyinka waxayna isticmaali kartaa isla jaantusyada. Xeerka awooda jibbaaraha m wuxuu ku saabsan yahay 2.2. Falanqaynta jabka daalka waxay muujinaysaa in fidinta dildilaaca farsamaysan iyo faafinta dildilaaca wadista labaduba ay yihiin jajab-jabka, joogitaanka joogtada ah ee hafnium oxide oogada sare ayaa sii xumeeyay iska caabinta dillaaca. Natiijooyinka la helay waxay muujinayaan in halbeeg awoodeed oo awood leh uu ku gaari karo isku mid ahaanshaha loo baahan yahay ee xaalado badan oo loading ah iyo qaabeynta joomatari, taas oo bixisa sharraxaad midaysan oo ku saabsan daalka heerkulka-farsamada ee qaababka xusuusta, taas oo lagu qiyaaso awoodda wadista.
Jaantuska 4 Sawirka SEM ee jabka NiTiHf DCT ka dib 180 ℃ tijaabada koritaanka daalka farsamada
Jaantuska 5 Jajab sawirka SEM ee muunada NiTiHf DCT ka dib wadida daalka tijaabada koritaanka dillaaca iyadoo culayska joogtada ah ee 250 N
Marka la soo koobo, warqadani waxay qabataa tijaabooyinka korriinka daalka daalka ee farsamaysan saafiga ah ee NiTiHf ee qaniga ku ah heerkulka sare ee alloys xusuusta markii ugu horeysay. Iyada oo ku saleysan is dhex galka meertada, nooca Paris awood-sharci muujinta koritaanka ayaa la soo jeediyay si ay ugu haboonaato heerka koritaanka dildilaaca daalka ee tijaabo kasta oo hoos timaada halbeeg